物性参数
测试方法见下表，具体数值以原厂技术资料为准。
左右滑动表格，查看完整数值与测试条件。
| 性能指标 | 典型数值 | 测试方法 |
|---|---|---|
| 熔体体积流动速率（MVR）（190 °C / 2.16 kg） | 21 cm³/10min | ISO 1133 |
| 熔体质量流动速率（MFR）（190 °C / 2.16 kg） | 25 g/10min | ISO 1133 |
| 成型收缩率（平行） | 1.9 % | ISO 294-4 |
| 成型收缩率（垂直） | 1.9 % | ISO 294-4 |
| 拉伸模量 | 3200 MPa | ISO 527-1/-2 |
| 屈服应力 | 71 MPa | ISO 527-1/-2 |
| 屈服应变 | 12 % | ISO 527-1/-2 |
| 标称断裂应变 | 23 % | ISO 527-1/-2 |
| 弯曲模量 | 3000 MPa | ISO 178 |
| Tensile creep modulus, 1h | 2800 MPa | ISO 899-1 |
| Tensile creep modulus, 1000h | 1500 MPa | ISO 899-1 |
| Charpy impact strength, 23°C | 200 kJ/m² | ISO 179/1eU |
| Charpy impact strength, -30°C | 200 kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 7.5 kJ/m² | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 6.5 kJ/m² | ISO 179/1eA |
| Izod notched impact strength, 23°C | 7 kJ/m² | ISO 180/1A |
| Izod notched impact strength, -40°C | 8 kJ/m² | ISO 180/1A |
| Hardness, Rockwell, M-scale | 92 | ISO 2039-2 |
| Hardness, Rockwell, R-scale | 120 | ISO 2039-2 |
| Ball indentation hardness, H 961/30 | 170 MPa | ISO 2039-1 |
| Poisson's ratio | 0.37 | |
| Melting temperature, 10°C/min | 178 °C | ISO 11357-1/-3 |
| Temp. of deflection under load, 1.8 MPa | 94 °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 162 °C | ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h, 50N | 160 °C | ISO 306 |
| Coeff. of linear therm. expansion, parallel | 120 E-6/K | ISO 11359-1/-2 |
| Coeff. of linear therm. expansion, normal | 120 E-6/K | ISO 11359-1/-2 |
| Eff. thermal diffusivity | 8E-8 m²/s | |
| RTI, electrical, 0.75mm | 50 °C | UL 746B |
| RTI, electrical, 1.5mm | 110 °C | UL 746B |
| RTI, electrical, 3mm | 110 °C | UL 746B |
| RTI, impact, 0.75mm | 50 °C | UL 746B |
| RTI, impact, 1.5mm | 85 °C | UL 746B |
| RTI, impact, 3mm | 90 °C | UL 746B |
| RTI, strength, 0.75mm | 50 °C | UL 746B |
| RTI, strength, 1.5mm | 90 °C | UL 746B |
| RTI, strength, 3mm | 95 °C | UL 746B |
| Burning Behav. at 1.5mm nom. thickn. | HB | IEC 60695-11-10 |
| Burning Behav. at thickness h（0.8 mm） | HB | IEC 60695-11-10 |
| Oxygen index | 23 % | ISO 4589-1/-2 |
| Glow Wire Flammability Index, 1mm | 550 °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 2mm | 550 °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 3mm | 550 °C | IEC 60695-2-12 |
| FMVSS Class | B | ISO 3795 (FMVSS 302) |
| Burning rate, Thickness 1 mm | 39 mm/min | ISO 3795 (FMVSS 302) |
| Hot Wire Ignition, 0.75mm | 8 s | UL 746A |
| Relative permittivity, 100Hz | 3.8 | IEC 62631-2-1 |
| Relative permittivity, 1MHz | 3.8 | IEC 62631-2-1 |
| Dissipation factor, 1MHz | 50 E-4 | IEC 62631-2-1 |
| Volume resistivity | 1E12 Ohm.m | IEC 62631-3-1 |
| Surface resistivity | >1E15 Ohm | IEC 62631-3-2 |
| Comparative tracking index | 600 | IEC 60112 |
| Humidity absorption, 2mm | 0.4 % | Sim. to ISO 62 |
| Water absorption, 2mm | 1.4 % | Sim. to ISO 62 |
| 密度 | 1420 kg/m³ | ISO 1183 |
| Emissions | <8 mg/kg | VDA 275 |
| Emission of organic compounds | 7.8 µgC/g | VDA 277 |
| Fogging, G-value (condensate) | 0.61 mg | ISO 6452 |
| 注塑加工 / 干燥温度 | 80 °C | |
| 注塑加工 / 除湿干燥时间 | 2 - 4 h | |
| 注塑加工 / 加工含水率 | ≤0.2 % | |
| 注塑加工 / 建议熔体温度 | 215 °C | |
| 注塑加工 / 最低熔体温度 | 210 °C | |
| 注塑加工 / 最高熔体温度 | 220 °C | |
| 注塑加工 / Max. screw tangential speed | 0.3 m/s | |
| 注塑加工 / 建议模具温度 | 90 °C | |
| 注塑加工 / 最低模具温度 | 80 °C | |
| 注塑加工 / 最高模具温度 | 100 °C | |
| 注塑加工 / 保压压力范围 | 80 - 100 MPa | |
| 注塑加工 / 保压时间 | 8 s/mm | |
| 注塑加工 / 可选退火时间 | 30 min/mm | |
| 注塑加工 / 退火温度 | 160 °C |
产品亮点
- 可联系咨询具体性能与选型要求。
典型应用
- 具体用途请结合原厂资料与实际工况确认。
选材建议
选型请结合工况及对应牌号的原厂技术资料；采购价格、货源和交期请联系确认。
产品介绍
Delrin 900P为通用低黏度均聚甲醛，专门面向多腔模具和薄壁注塑。其加工定位适合需要关注充模条件的零件。
配方同时改善加工热稳定性，并具有较低的挥发性有机物排放。工艺选择应结合流道布局、壁厚和熔体停留时间进行，低VOC并不意味着零排放。
本页物性和注塑参数采用 Delrin 900P NC010 参考资料。其他颜色应核对对应版本，不能把参考色号视为实际供货颜色；挥发物和雾化数据还应按所用资料版本及测试条件比较。