物性参数
测试方法见下表，具体数值以原厂技术资料为准。
左右滑动表格，查看完整数值与测试条件。
| 性能指标 | 典型数值 | 测试方法 |
|---|---|---|
| 熔体体积流动速率（MVR）（190 °C / 2.16 kg） | 13 cm³/10min | ISO 1133 |
| 熔体质量流动速率（MFR）（190 °C / 2.16 kg） | 15 g/10min | ISO 1133 |
| 成型收缩率（平行） | 2.0 % | ISO 294-4 |
| 成型收缩率（垂直） | 1.9 % | ISO 294-4 |
| 拉伸模量 | 3100 MPa | ISO 527-1/-2 |
| 屈服应力 | 70 MPa | ISO 527-1/-2 |
| 屈服应变 | 17 % | ISO 527-1/-2 |
| 标称断裂应变 | 30 % | ISO 527-1/-2 |
| 弯曲模量 | 3000 MPa | ISO 178 |
| 弯曲强度 | 77 MPa | ISO 178 |
| Flexural Stress at 3.5% | 78 MPa | ISO 178 |
| Charpy impact strength, 23°C | 260 kJ/m² | ISO 179/1eU |
| Charpy impact strength, -30°C | 260 kJ/m² | ISO 179/1eU |
| Charpy notched impact strength, 23°C | 9 kJ/m² | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 8 kJ/m² | ISO 179/1eA |
| Izod notched impact strength, 23°C | 8 kJ/m² | ISO 180/1A |
| Izod notched impact strength, -40°C | 8 kJ/m² | ISO 180/1A |
| Hardness, Rockwell, M-scale | 92 | ISO 2039-2 |
| Hardness, Rockwell, R-scale | 120 | ISO 2039-2 |
| Poisson's ratio | 0.37 | |
| Melting temperature, 10°C/min | 178 °C | ISO 11357-1/-3 |
| Temp. of deflection under load, 1.8 MPa | 90 °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 163 °C | ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h, 50N | 160 °C | ISO 306 |
| Vicat softening temperature, 50°C/h 10N | 174 °C | ISO 306 |
| Coeff. of linear therm. expansion, parallel | 110 E-6/K | ISO 11359-1/-2 |
| Coeff. of linear therm. expansion, normal | 120 E-6/K | ISO 11359-1/-2 |
| Thermal conductivity | 0.4 W/(m K) | ISO 22007-2 |
| RTI, electrical, 0.75mm | 50 °C | UL 746B |
| RTI, impact, 0.75mm | 50 °C | UL 746B |
| RTI, strength, 0.75mm | 50 °C | UL 746B |
| Burning Behav. at thickness h（0.8 mm） | HB | IEC 60695-11-10 |
| FMVSS Class | B | ISO 3795 (FMVSS 302) |
| Burning rate, Thickness 1 mm | 21 mm/min | ISO 3795 (FMVSS 302) |
| Relative permittivity, 100Hz | 3.8 | IEC 62631-2-1 |
| Relative permittivity, 1MHz | 3.8 | IEC 62631-2-1 |
| Dissipation factor, 100Hz | 21 E-4 | IEC 62631-2-1 |
| Dissipation factor, 1MHz | 56 E-4 | IEC 62631-2-1 |
| Volume resistivity | >1E13 Ohm.m | IEC 62631-3-1 |
| Surface resistivity | 2E13 Ohm | IEC 62631-3-2 |
| Comparative tracking index | 600 | IEC 60112 |
| Humidity absorption, 2mm | 0.2 % | Sim. to ISO 62 |
| Water absorption, 2mm | 1.2 % | Sim. to ISO 62 |
| Water absorption, Immersion 24h | 0.5 % | Sim. to ISO 62 |
| 密度 | 1420 kg/m³ | ISO 1183 |
| Fogging, G-value (condensate) | 0.2 mg | ISO 6452 |
| 注塑加工 / 干燥温度 | 80 °C | |
| 注塑加工 / 除湿干燥时间 | 2 - 4 h | |
| 注塑加工 / 加工含水率 | ≤0.2 % | |
| 注塑加工 / 建议熔体温度 | 215 °C | |
| 注塑加工 / 最低熔体温度 | 210 °C | |
| 注塑加工 / 最高熔体温度 | 220 °C | |
| 注塑加工 / Max. screw tangential speed | 0.3 m/s | |
| 注塑加工 / 建议模具温度 | 90 °C | |
| 注塑加工 / 最低模具温度 | 80 °C | |
| 注塑加工 / 最高模具温度 | 100 °C | |
| 注塑加工 / 保压压力范围 | 80 - 100 MPa | |
| 注塑加工 / 保压时间 | 8 s/mm | |
| 注塑加工 / 可选退火时间 | 30 min/mm | |
| 注塑加工 / 退火温度 | 160 °C |
产品亮点
- 抗紫外线
- 耐候
- 润滑
典型应用
- 具体用途请结合原厂资料与实际工况确认。
选材建议
选型请结合工况及对应牌号的原厂技术资料；采购价格、货源和交期请联系确认。
产品介绍
Delrin 527UV是一款中等黏度均聚甲醛，专为汽车内饰应用开发，采用紫外线稳定配方。它关注较长时间光照后的机械性能与热稳定性。
该牌号可通过注塑加工。零件设计应将光照条件、温度和受力要求结合起来，评估实际使用环境下的表现。
本页物性和注塑参数参考 Delrin 527UV NC010 资料。所列数值用于该版本的选材比较，其他颜色应查阅对应数据；参考色号不代表实际供货颜色。